Casting Tolerance Reference Chart

casting measure

Size ange (mm) CT Category
From To 3 4 5 6 7 8 9
10.00 0.18 0.26 0.36 0.52 0.74 1.00 10.00 1.50
16.00 0.20 0.28 0.38 0.54 0.78 1.10 16.00 1.60
25.00 0.22 0.30 0.42 0.58 0.82 1.20 25.00 1.70
40.00 0.24 0.30 0.46 0.64 0.90 1.30 40.00 1.80
63.00 0.26 0.36 0.50 0.70 1.00 1.40 63.00 2.00
100.00 0.28 0.40 0.56 0.78 1.10 1.60 100.00 2.20
160.00 0.30 0.44 0.62 0.88 1.20 1.80 160.00 2.50
250.00 0.34 0.50 0.70 1.00 1.40 2.00 250.00 2.80
400.00 0.40 0.56 0.78 1.10 1.60 2.20 400.00 3.20
630.00 0.64 0.90 1.20 1.80 2.60 630.00 3.60
1,000.00 1.00 1.40 2.00 2.80 1,000.00 4.00

 

NOTES:

1.  Above dimensions and tolerances are in Millimeters (mm).

2.  Tolerances shown represent total tolerance band. For example, a 50mm dimension under a CT5 tolerance (=0.5mm) means 50mm +/-0.25mm.

3.  Tolerances in the above table should be used as a guide only. Actual tolerances achieved may be looser or tighter, depending on specific tooling and casting features.

China and Japan Ferrous Metal Standard comparison
China and Japan Ferrous Metal Standard comparison
China and Japan Ferrous Metal Standard comparison
Read More
GGG40-Ductile Iron
GGG40 - Ductile Iron
Cast iron GGG40 is a low grade of ductile iron. Leesh Holdings' foundry has pouring this material for...
Read More
DIN 50150 hardness Conversion Sheet
DIN 50150 :Vickers hardness, Brinell hardness and Rockwell hardness Conversion Sheet
  Noted: This sheet only for your reference, please don’t take this as your production, inspection...
Read More
Common Ductile Iron Standards Comparison
Common Ductile Iron Standards Comparison
Common Ductile Iron Standards Comparison
Read More
ductile cast iron inspection
Detailed explanation of the Inspection method of ductile cast iron
Metallography Inspection Hardness Inspection Pressure Testing Ultrasonic inspection
Read More
manual moulding and machine moulding
The introduction of manual moulding and machine moulding of sand casting
Manual moulding Manual moulding refers to the moulding process of using hand or hand tools to complete...
Read More
Casting Alloy fluidity during casting process
Casting Alloy fluidity during casting process
Beased on many years casting expericne ,Leesh casting engineer team sharing some knowledge of the Casting...
Read More
sand casting auto line
Precision Casting: A Comprehensive Guide to the Process, Materials, and Applications
Precision casting, also known as investment casting or lost wax casting, is a manufacturing process that...
Read More
C86500 Is a kind of copper alloy material, mainly used in chemical machinery and equipment, with high electrical conductivity, thermal conductivity, corrosion resistance and mechanical strength characteristics. C86500 Copper by adding the right amount of tin, zinc and other elements, significantly improve the corrosion resistance and mechanical strength of the material, so that it can maintain long-term stability and durability in the face of common acid, alkali, salt and other corrosive media in the chemical environment . In addition, C86500 copper material also has good processing performance, suitable for Leesh sand casting, investment casting, forging, and machining processes, can meet the needs of complex chemical equipment.
C86500-Manganese Bronze
C86500 Is a kind of copper alloy material, mainly used in chemical machinery and equipment, with high...
Read More
Casting Tolerance Reference Chart
Size ange (mm) CT Category From To 3 4 5 6 7 8 9 10.00 0.18 0.26 0.36 0.52 0.74 1.00 10.00 1.50 16.00...
Read More
Scroll to Top